Nanostructured melt-spun Sm(Co,Fe,Zr,B)(7.5) alloys for high-temperature magnets (Journal article)

Makridis, S. S./ Litsardakis, G./ Efthimiadis, K. G./ Papathanasiou, G./ Panagiotopoulos, I./ Hofinger, S./ Fidler, J./ Hadjipanayis, G. C./ Niarchos, D.


High coercivity, the highest for Cu-free 2: 17 Sm-Co ribbons, has been obtained in as-spun (H-c = 21.1 kOe) and short time annealed (H-c = 23.2 kOe) samples of Sm(CobalFezZryBx)(7.5) alloys, with varying B, Zr, and Fe content (x = 0-0.06, y = 0-0.16, z = 0.08-0.3) and wheel speed. In as-spun samples, the TbCu7 type structure and in annealed samples the Th2Zn17 and CaCu5 type structures is observed, plus fee Co as minority phase is observed. Reduced remanence (M-r/M-s) is higher than 0.7. High-temperature magnetic measurements show very good stability above 300 degreesC with coercive field as high as 5.2 kOe at 330 degreesC. For annealed Sm(CobalFe0.3Zr0.02B0.04)(7.5), very good loop squareness and high maximum energy product of 10.7 MGOe have been obtained. Increasing Zr content results in less uniform microstructure of annealed ribbons.
Institution and School/Department of submitter: Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών
Keywords: coercive force,hard magnetic materials,permanent magnets
URI: http://olympias.lib.uoi.gr/jspui/handle/123456789/14248
ISSN: 0018-9464
Link: <Go to ISI>://000185722100213
Appears in Collections:Άρθρα σε επιστημονικά περιοδικά ( Ανοικτά)

Files in This Item:
File Description SizeFormat 
Panagiotopoulos-2003-Nanostructured melt-spun.pdf88.97 kBAdobe PDFView/Open    Request a copy



 Please use this identifier to cite or link to this item:
http://olympias.lib.uoi.gr/jspui/handle/123456789/14248
  This item is a favorite for 0 people.

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.