Magnetic-Properties and Microstructure of Melt-Spun Nd-Fe-Ga-B Alloys (Journal article)
Panagiotopoulos, I./ Murthy, A. S./ Hadjipanayis, G. C.
The magnetic and microstructural properties of melt-spun Nd18Fe76-XGaXB6 alloys have been studied as a function of Ga content. Coercivities of 17 kOe were obtained in underquenched samples having a large grain size of 500 nm. Samples prepared at wheel speeds of 15-19 m/sec, as well as overquenched (40 m/sec) and subsequently annealed, gave coercivities of around 20 kOe with no significant improvement of H-c upon Ga substitution. In Ga-free samples prepared by annealing highly overquenched ribbons (at 60 m/sec) only moderate coercive fields could be achieved (14 kOe). These samples had grain sizes of 70-100 nm. However Ga substituted samples prepared under the same conditions have a fine grain structure consisting of unequiaxed grains with size around 20 nm and show coercivities up to 23 kOe.
|Institution and School/Department of submitter:||Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών|
|Link:||<Go to ISI>://A1995TD55800056|
|Appears in Collections:||Άρθρα σε επιστημονικά περιοδικά ( Ανοικτά)|
Files in This Item:
There are no files associated with this item.
Please use this identifier to cite or link to this item:This item is a favorite for 0 people.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.