Crystallization behavior of melt-spun NdxFe93-xNb1B6 alloys (Journal article)

Withanawasam, L./ Panagiotopoulos, I./ Hadjipanayis, G. C.


The crystallization behavior of NdxFe93-xNb1B6 melt-spun ribbons was investigated using calorimetric techniques. The crystallization products were identified by X-ray diffraction and thermomagnetic measurements. Samples with x greater than or equal to 10 crystallize directly from amorphous to a mixture of Nd2Fe14B and alpha-Fe phases. For 10< x <7, the final mixture of 2:14:1 and alpha-Fe phases is obtained through a two stage crystallization where the intermediate metastable Nd2Fe23B3 and Nd3Fe62B14 phases are produced at the initial crystallization. In samples with 7< x <4 the intermediate phase is Nd3Fe62B14. No metastable phases were observed in samples containing less than 3 at. % Nd although the calorimetric measurements indicated a two-step crystallization process.
Institution and School/Department of submitter: Πανεπιστήμιο Ιωαννίνων. Σχολή Θετικών Επιστημών. Τμήμα Μηχανικών Επιστήμης Υλικών
Keywords: magnets
URI: http://olympias.lib.uoi.gr/jspui/handle/123456789/13794
ISSN: 0018-9464
Link: <Go to ISI>://A1996VM25900048
Appears in Collections:Άρθρα σε επιστημονικά περιοδικά ( Ανοικτά)

Files in This Item:
There are no files associated with this item.



 Please use this identifier to cite or link to this item:
http://olympias.lib.uoi.gr/jspui/handle/123456789/13794
  This item is a favorite for 0 people.

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.